wear resistant coatings > desulfuration pipe liner ceramic repair putty epoxy coating

desulfuration pipe liner ceramic repair putty epoxy coating

BD7056 desulfurization pipeline lining ceramic repair putty epoxy compound coating material

Product description:
BD7056 desulfuration pipe lining ceramic putty repair compound material is specifically for the protection of the desulfurization
pipeline system developed a kind of special corrosion & abrasion resistant coating.it is the high performance,high temperature resistant,
wear resistant and corrosion resistant polymeric ceramic material which compounded by high performance abrasion resistant,
corrosion resistant material and modified toughening heat resistant resin.Xiangyang hundred Shield Coating has the core technology,
exclusive production.

Product packaging photo of BD7056 desulfuration slurry pipe liner ceramic repair putty compound epoxy coating

Product features:
1.With good performance of wear resistant and corrosion resistant,it doesn’t craze for long-terms hot-water soak,can sustained and
effective protect desulfurization pipeline from erosive wear and invalidation,thus make the equipment long-terms reliable operation.
2.With very high bonding strength to metal and resin type substrates.
3.With good toughness,doesn’t craze.
4.Suitable for the protecting of high temperature erosive wear and corrosion working condition.
5.Hot water resistant,acid resistant,alkali resistant and steam resistant.
6.Don't drip and slip,the construction is convenient,the coating surface after curing is smooth.

Performance index:

Product name	Physical states	Operation time limit (25℃)	Curing time (25℃)	Range of application
BD7056 desulfuration pipe lining ceramic repair putty compound material	Paste	40 min	24 hours	be exclusively used in the repairing of desulfuration pipe and the preparation of wear & corrosion resistant coating on the surface of desulfuration pipeline

Color	Density (g/cm3)	Compressive strength (Mpa) GB1041-2008	Tensile strength (Mpa) GB6329-2008	Shear strength (Mpa) GB7124-2008	Bending strength (Mpa) GB1042-1999	Hardness after curing （Shore D） ASTM-D-2556	Working temperature (25℃)
Gray	2.3	146	51	20	59	139	-60-150

How to use:
1.Surface treatment:Do the coarsening treatment for the pending-repair parts,(polishing with angle grinder or sand blasting etc.),
then clean it by cleaning agent,the surface after this treatment should be the one coarse,dry and fresh substrates,should be no
greasy dirt and dust.

2.The preparation:Mix the A and B two components of BD7056 desulfurization pipeline liner ceramic repair putty compound material
uniformly based on weight ratio A:B=4:1,and use it up within 40 min,generally it is while construction and the preparation,each time
the largest preparation quantity can’t be more than 4Kg,too much adhesive is solidified too fast,hasn’t been used up until the partial
adhesive has solidified and can’t be used,according to the actual temperature,the preparation can be properly more in winter,
properly be less in summer,if the temperature is too low,can properly heat up the A component to reduce the viscosity for easy to configure.

3.Coating:The suitable coating thickness of BD7056 desulfurization pipe lining ceramic repair putty compound is 2-8mm,should make the
well mixed material be coating on the surface of the substrates,the coating should be compacted,make it infiltrate fully with the substrates.
Repair the surface to be smooth after the coating is coated in the suitable size,this material can’t do machining,should pay attention to
controlling the coating thickness to avoid appearing interference phenomenon in the assembly.

4.Curing:It can be put into using after curing for 24 hours at the temperature of 25 degree,when the temperature is below 15 degree,
the coating can’t be curing fully,should heat it up to the temperature of 80 degree and keep this temperature for 2 hours to promote the
coating to be curing fully after the coating initial curing,can use the iodine tungsten lamp to do irradiation heating with 40cm distance from
the coating.

Transportation storage:
Sealed storage in the cool and dry place.The warranty period is 12 months.Avoid placing it upside down, knocking against and transporting it
as a non-dangerous product during transportation.

Packaging specifications:
Two components,20Kg/group,packed in a plastic drum, A component: 16Kg/drum, B component: 4Kg/drum.